| Element | Content(%) |
|---|---|
| Chromium, Cr | 17-19 |
| Nickel, Ni | 8 - 10 |
| Manganese, Mn | 2 |
| Silicon, Si | 1.00 |
| Carbon, C | 0.15 |
| Sulfur, S | 0.03 |
| Phosphorous, P | 0.045 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 620 MPa | 89900 psi |
| Yield strength (@strain 0.200%) | 275 MPa | 39900 psi |
| Elastic modulus | 193 GPa | 28000 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 55% | 55% |
| Hardness, Brinell (converted from Rockwell B hardness) | 147 | 147 |
| Hardness, Knoop (converted from Rockwell B hardness) | 164 | 164 |
| Hardness, Rockwell B | 85 | 85 |
| Hardness, Vickers (converted from Rockwell B hardness) | 147 | 147 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |
AISI 302 Equivalent Grade / Specifications
- AMS 5515
- AISI 302
- AMS 5516
- AMS 5636
- AMS 5637
- AMS 5688
- ASME SA240
- ASTM A167
- ASTM A240
- ASTM A276
- ASTM A313
- ASTM A314
- ASTM A368
- ASTM A473
- ASTM A478
- ASTM A479
- ASTM A492
- ASTM A493
- ASTM A511
- ASTM A550
- ASTM A554
- ASTM A666
- FED QQ-S-763
- FED QQ-S-766
- FED QQ-W-423
- ASTM A580
- MIL SPEC MIL-S-862
- SAE 30302
- SAE J230
- SAE J405
- AMS 5788
- DIN 1.4319
- MIL S-7720
- QQ S763
- QQ S766