AISI 321H
Stainless steel 321H is a general purpose austenitic stainless steel that is stabilized against carbide precipitation and designed to work within the carbide precipitation temperature range 427 to 816°C (800 to 1500°F). It is non-magnetic in the annealed condition and can be hardened only by cold working. Titanium is added to the alloy's composition to suppress grain boundary chromium carbide precipitation and reduce susceptibility to intergranular corrosion.
| Element | Content(%) |
|---|---|
| Iron, Fe | Balance |
| Chromium, Cr | 17-19 |
| Nickel, Ni | 9-12 |
| Manganese, Mn | 2 |
| Silicon, Si | 1 |
| Titanium, Ti | 0.35 |
| Phosphorous, P | 0.045 |
| Carbon, C | 0.04-0.10 |
| Sulfur, S | 0.03 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 480 MPa | 69600 psi |
| Yield strength | 205 MPa | 29700 ksi |
| Elongation at break | 29% | 29% |
| Hardness, Brinell | ≤187 | ≤187 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |