| Element | Content(%) |
|---|---|
| Chromium, Cr | 14-16 |
| Silicon, Si | 1 |
| Manganese, Mn | 1 |
| Carbon, C | 0.12 |
| Phosphorous, P | 0.04 |
| Sulfur, S | 0.03 |
| Iron, Fe | Balance |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength (annealed) | 490 MPa | 71068 psi |
| Yield strength (annealed/ @strain 0.200 %) | 310 MPa | 44961psi |
| Modulus of elasticity | 200 GPa | 29007 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (In 2", 50% cold worked) | 30% | 30% |
| Hardness, Rockwell B (annealed) | 88 | 88 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |