| Element | Content(%) |
|---|---|
| Iron, Fe | Balance |
| Chromium, Cr | 16-18 |
| Manganese, Mn | 1 |
| Silicon, Si | 1 |
| Molybdenum, Mo | 0.75 |
| Carbon, C | 0.60-0.75 |
| Sulfur, S | 0.03 |
| Phosphorous, P | 0.04 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 725-1790 MPa | 105000 - 260000 psi |
| Yield strength (@strain 0.200 %) | 415-1650 MPa | 60200 - 239000 psi |
| Modulus of elasticity | 204 - 215 GPa | 29600 - 31200 ksi |
| Elongation at break (in 50 mm) | 5- 20% | 5- 20% |
| Hardness, Rockwell B | 95 | 95 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |